Issue 41

F. Berto et alii, Frattura ed Integrità Strutturale, 41 (2017) 79-89; DOI: 10.3221/IGF-ESIS.41.12 81 and a mean value of 0.09 mm with a very reduced scatter has been obtained. The precision ensured by the adopted method is about ± 5% of the measured quantity. The typical V-notch profile characterised by two rectilinear flanks tangent to the notch tip radius is reported in Fig. 1b, for an example of the tested samples. To remove any scratches or processing marks on the surface, all specimens were polished before the fatigue test. (a) (b) Figure 1: (a) Geometries of smooth and sharply notched specimens and (b) examples of tested specimens. E XPERIMENTAL RESULTS FROM FATIGUE TESTS he experimental fatigue tests have been carried out by means of a MTS 809 servo-hydraulic bi-axial testing device (± 100 kN, ± 1100 Nm, ± 75mm/± 55°) under load control conditions. In particular, a MTS load cell with ± 0.5 % error at full scale has been employed to evaluate the nominally applied loads. A test frequency between 10 and 15 Hz has been adopted as a function of the applied load level. All in all, 19 different fatigue test series are performed, according to the parameters reported below:  Four series of fatigue tests on smooth and sharply notched samples subjected to pure tension and pure torsion fatigue loadings, with a nominal load ratio R = -1;  Four series of fatigue tests on smooth and sharply notched samples subjected to pure torsion fatigue loading, with nominal load ratios R = 0 and 0.5;  Three series of fatigue tests on smooth samples subjected to pure torsion fatigue loading, with nominal load ratios R = 0.25, -2 and -3;  Four series of fatigue tests on sharply notched samples subjected to combined tension and torsion loadings, at a constant biaxiality ratio λ = 0.6. Two load ratios, R = 0 and R = -1 (referred separately to the normal and shear stress components), and two phase angles, Ф = 0° (proportional loadings) and Ф = 90° (non-proportional loadings), are employed;  Four series of fatigue tests on sharply notched samples subjected to combined tension and torsion loading, at a constant biaxiality ratio λ = 2.0. Also in this case, two load ratios, R = 0 and R = -1, and two phase angles, Ф = 0° (proportional loadings) and Ф = 90° (non-proportional loadings), are adopted.  d = 6 mm  = 0.1 mm  24 90°  = 100 mm  24 150 mm T