Issue 41

D.-Q. Wang et alii, Frattura ed Integrità Strutturale, 41 (2017) 143-148; DOI: 10.3221/IGF-ESIS.41.20 145 (OLR) was set as 1.2. The cyclic loaded tests were interrupted every five cycles to take images, from which crack growth length and strain distribution were measured. SEM images were taken at two magnifications, i.e., 500X for strain measurement and 5000X for crack length measurement. As shown in Fig. 2, after 40 cycles of constant amplitude testing, an overload cycle was then exerted, followed by another 40 cycles of constant amplitude loading. Special attention was paid to the overload cycle, and the cycle just before and after the overload, by taking more images at an increment of 5% of P max . Figure 2 : The loading scheme of the experiment (the 40 cycles before and after the overload cycle is a loading block contains 8 sub- block with 5 cycles for each of them) Digital image correlation The in-plane displacement and strain were analyzed by commercial DIC software (VIC-2D 2009, Correlated Solutions). The un-deformed image at zero load was set as the reference image and the deformed images were target ones. In this work, the intrinsic microstructures of the steel with an average characteristic size of 10  m were regarded as speckles needed by DIC for tracking in-plane deformation. Suitable parameters such as subset size and step size were selected to be 31 pixels and 5 pixels, respectively. The strain measurement based on intrinsic microstructures as speckles was found with sufficient resolution in our previous work on a steel with similar microstructures [13]. R ESULTS AND DISCUSSION Crack growth morphologies ig. 3 shows the crack growth morphologies during the overload process and strain distribution based on DIC measurement. All the SEM images shown here are taken at peak load. The fatigue crack is just at a grain boundary before the overload cycle, as observed in Fig. 3a. The crack then gets across the grain boundary at the peak load of overloading and is branched (Fig. 3b). Fig. 3c shows the extension of branched cracks after overload cycle. Figs. 3d, 3e and 3f denote the strain distribution before, at and after the overload. The strain distribution near crack tip is varied, and the shape of highly concentrated zone from which plastic zone size is determined is also changed with overload. It seems that the strain is localized at and around the grain boundary, indicating the potential of next cracking under constant amplitude loading. Crack tip strain evolution The normal strains perpendicular to the crack plane ahead of the crack tip was extracted after correlation procedure. The reference image was taken at the minimum load at N OL -1 cycle. The data points stands for the strain values with a distance of 50  m away from the crack tip. The strain evolution during the three full cycles is shown in Fig. 4. Strain loops are observed in the pre-overload and post-overload cycle, while the overload induces large residual strain at the crack tip. Time 5 cycles R T 0 T 1 T 8 40 cycles 5 cycles T 1 T 8 40 cycles overload R F