P. Jinchang et alii, Frattura ed Integrità Strutturale, 36 (2016) 130-138; DOI: 10.3221/IGF-ESIS.36.13 133 mixing amount was too large, strength improved with a limited amplitude and even decreased slightly. There were two reasons. First, water demand increased, resulting in high water-binder ratio. Secondly, nanomaterial failed to disperse evenly and thus aggregated, lowering evenness of UHPCC [12]. Hence mixing amount of nanomaterial should be controlled within certain scope. We thought the best mixing amount of nano-CaCO 3 was 3% ~ 5%. Compared to test specimen without nano-SiO 2 or with nano-SiO 2 only, test specimen added with nano-SiO 2 and nano-CaCO 3 had significantly improved strength; NSC 3 test specimen with curing age of 90 d could have a compressive strength of 107 MPa and a flexural strength of 20 MPa. Nano-SiO 2 can promote hydration of cement and C-S-H gel generates when nano-SiO 2 reacts with cement hydration products. Though nano-CaCO 3 has low activity, it can be used for filling spaces inside composite material and thus improves density. (1) Compressive strength (2) Rapture strength Figure 2 : Compressive and rapture strength of UHPCC with different curing age. Hydration Heat Analysis Hydration heat test was carried out three days after processing the above four kinds of UHPCC with water and the results are shown in Fig. 3. It can be seen from Fig. 3 that, heat curve of four materials were similar; hydration acceleration period of hydration test specimen mixed with nano-SiO 2 was from 10 th h to 20 th h; double-doped materials which had larger mixing amount of nano-CaCO 3 had hydration acceleration and exothermic peak earlier. It indicates that, double mixture of nanomaterials can accelerate hydration. Figure 3 : Hydration heat curve for UHPC test specimen. XRD Quantitative Analysis Traditional XRD methods usually used for quantitative analysis such as external standard method, internal standard method, K value method, and adiabatic method all aims at analyzing single hkl diffracted ray or hkl diffraction family. Sample of cement based composite material with multiple phases and complex diffraction xrd pattern will bring great difficulty to quantitative analysis due to severely overlapped spectral peak and preferentially orienting effect. Rietveld whole power pattern fitting may transform the status if being applied in XRD pattern analysis. The structure depended method can accurately make an analysis on diffraction peaks and comparison of diffraction strength of different phrase. Specialized cement phase structure database which can be used for analyzing cement clinker and phase of mineral admixtures has been established after years of research works.