Issue 35

A. Vshivkov et alii, Frattura ed Integrità Strutturale, 35 (2016) 57-63; DOI: 10.3221/IGF-ESIS.35.07 62 corresponds the heat flux calculated by treatment of surface temperature evolution measured by independent way. Based on the data presented in Fig. 8 we can conclude that there is a linear relation between crack rate and product of crack length and heat power from the crack tip. This conclusion was confirmed by the results obtained with the other sample geometries presented in Fig. 4. All tests were carried out with constant stress amplitude. Figure 7 : The characteristic dependence of the power of heat flux from the crack tip. Figure 8 : The relation between fatigue crack rate and the fatigue crack length multiplied by the power of heat flow. C ONCLUSION he paper describes the structure and performance of the heat flux sensor which was designed based on the Seebeck effect. This sensor can be used to analyze the energy balance of the material during the deformation process either in combination with the method of infrared thermography (for its verification), or independently. In the case of its independent usage the loss of information about the spatial distribution of the heat is compensated by the possibility of long-term measurements. With this technique a comprehensive investigation into the processes of energy dissipation during the propagation of fatigue cracks in metal alloys was done. The analysis of the results allowed putting forward the hypothesis for a linear relationship between the rate of fatigue crack propagation and the product of the rate of energy dissipation by the length of the crack. The developed method can be used to calculate the value of the dissipated energy at any moment of the material lifetime. One of possible promising continuation of the work is a combination of this result with the calculation of applied energy. It could give us an opportunity to estimate a stored energy (cold work) of deformation. The stored energy is widely used to formulate a criterion of material failure [5, 6]. Thus, the proposed method can be applied to assess the state of the material. A CKNOWLEDGMENTS his work was supported by The Perm Regional Government № С-26/619 and grants RFBR (№ 14-01-96005, 14- 01-00122). R EFERENCES [1] Pradere, C., Joanicot, M., Batsale, J.-C., Toutain, J., Gourdon, C., Processing of temperature field in chemical microreactors with infrared thermography, QIRT Journal, 3 (2006) 117-135. [2] Izyumova, A. Yu., Plekhov, O. A., Vshivkov, A. N., Prokhorov, A. A., Uvarov, S. V., Studying the Rate of Heat Dissipation at the Vertex of a Fatigue Crack, Technical Physics Letters, 40(9) (2014) 810-812. [3] Kyhling, H., Spravochnik po fizike [Guide to Physics], Moscow, (1982). T T