Issue 35

M.V. Bannikov et alii, Frattura ed Integrità Strutturale, 35 (2016) 50-56; DOI: 10.3221/IGF-ESIS.35.06 55 a) b) Figure 8: Fracture surface of Ti Grade-4 a)-optical image, b) New View image. Roughness of fracture surfaces of samples with the surface fatigue crack (Fig. 9) was also investigated by interferometer New View 5010 and analyzed with correlation function (3). The correlation function detects only one slope across the fracture surface of both near and far from the crack initiation point. The value of the Hurst exponent calculated on linear part of the correlation function corresponds to the fractal dimension of the profile of the crack propagating through Paris law like in second zone in previous case. The accumulation defects zone typical to internal crack initiation is not detected. This shows fundamentally different mechanisms for the fatigue crack initiation in the bulk and on the surface of material. Figure 9: New view image of 2D- profile fracture surface of Ti Grade-4 with fatigue crack initiated from surface of the specimen. C ONCLUSIONS he analysis of scale-invariant properties of fracture surface allowed us to establish the qualitative difference in terms of the scale invariance (the Hurst exponent) of the surface roughness for the areas of crack initiation and propagation. The crack initiation area can be identified as the zone with pronounced multiscale defect interaction providing correlated behaviour over characteristic scale. The size of this zone and collective defect growth kinetics were studied in [10] and associated with special type of spatial-temporal defect organization named as collective blow-up mode of defects. The scenarios of crack nucleation (in the bulk of specimen for gigacycle load and at the surface for HCF) reflect qualitative different kinetics of collective behaviour of defects in mentioned regimes caused by typical size of defects and interaction length. However, the scenario of crack propagation under gigacycle regime corresponds to the Paris law that reflects the similarity in the mechanisms of plastic flow at the crack tip that still follows the stress induced singularity in term of the stress intensity factor increment. A CKNOWLEDGEMENTS his study was supported by the Russian Science Foundation, project No. 14-19-01173. T T