Issue 35

X.C. Arnoult et alii, Frattura ed Integrità Strutturale, 35 (2016) 509-522; DOI: 10.3221/IGF-ESIS.35.57 515 For D-D orientation (cf. Figure 6), API X80 steel developed some delamination cracks only at -20°C and the impact energy was comparable for the other two orientations at the same temperature. For the other test temperatures (from - 60°C to -100°C), cleavage fracture was the main failure mode for D-D specimen orientation (cf. Figure 7). For the authors, good resistance to impact of specimens with T-L and L-T orientation at ductile-brittle transition region is due to the capacity of delamination to take place during the failure process. Their assumption is reinforced by the fact that the impact energy dropped sharply below -60°C for the T-L and L-T oriented specimens and the only time when the D-D orientated specimens showed a similar magnitude of impact energy as T-L and L-T oriented specimens was when some delamination cracks were present during the failure process. R ELATIONSHIP BETWEEN METALLOGRAPHY AND DELAMINATION CRACKS s described in the two previous sections, heat treatment and specimen orientation have a strong effect on the occurrence of delamination cracking as one of the fracture modes. It seems obvious that microstructure and texture of the studied steels is an important factor in this process. Different steels with various microstructure and texture were investigated. Steels Code Microstructure HSLA steel [23] MC1, F2A Acicular ferrite MC2 Acicular ferrite MC3 Acicular ferrite MC4 Polygonal ferrite, Acicular ferrite C1B Polygonal ferrite, Acicular ferrite, Thin filament of Cementite along grain boundaries M1 Polygonal ferrite D=7µm, d=6µm, Acicular ferrite Pearlite HSLA steel [24] Banding of ferrite Banding of pearlite C-Mn steel [18] Ferrite Pearlite Average grain size = 6.8 µm Ultrafine grained C- Mn steel [18] Ferrite with globular Cementite particle in the grain Cementite located at ferrite grain boundaries Average grain size = 1.3 µm X100 steel [8] A Ferrite, Bainitic-Martensitic dual phase, Ferrite fraction: 20% B Ferrite and Bainitic-Martensitic dual phase, Ferrite fraction: 70% C Ferrite and Bainitic-Martensitic dual phase, Ferrite fraction: 75% D Deformed ferrite, Bainitic-Martensitic dual phase, Ferrite fraction: 20% HSLS [6, 7] Ferrite Lower bainite Carbides and nitrides API X80 [9] Coarse Allotriomorphics Ferrite, Pearlite, MA constituent, Bainite Micro-alloyed low carbon steel [10] Ferrite, Bainite 08Ch18N10T [25] Austenite Delta-Ferrite Table 3 : Different steels and their microstructure investigated for the understanding of delamination cracks. A