Issue 30

A. Martín-Meizoso et alii, Frattura ed Integrità Strutturale, 30 (2014) 14-22; DOI: 10.3221/IGF-ESIS.30.03 18 Figure 4 : Details of CAZ, at middle thickness of cut edge, showing Vickers’ hardness indentations. 0 50 100 150 200 250 300 350 400 0 500 1000 1500 2000 Vicker's HARDNESS (HV05, kg/mm 2 ) Distance fromoxy‐fuel cut (microns) Oxy‐Fuel cut of S460M, 25 mm Top (0.5 mm) Top (2.5 mm) Middle Bottom (2.5 mm) Bottom (0.5mm) Figure 5 : Micro-hardness profiles vs. distance from cut edge.