Issue 21

R. Valentini et alii, Frattura ed Integrità Strutturale, 21 (2012) 30-36; DOI: 10.3221/IGF-ESIS.21.04 32 R ESULTS esults of SSRT campaign are presented, as a function of time to failure and environment, in Table 2. Figures 2 to 3 show the measured stress as a function of time for the AISI 4340 and Maraging 250 respectively. From the curves of Fig. 3, it emerges as the shortest time to failure for AISI 4340 (551 s compared to 2490 s of the specimens loaded in air) was measured for the specimens subjected to painting and then stripped. Specimens, tested in salt solution, with and without galvanic coupling failed in comparable times. In particular, the specimens coupled to AISI 316 failed inside the galvanic coupling, even if externally to the exposed area. Fig. 4 (a) shows both the absence of necking and the ring of zinc corrosion products for one of the specimens involved in the latter test. Regarding Maraging 250, any of the curves related to the specimens loaded in corrosive environment differed significantly from the trend associated to the test performed in air. In detail, time to failure for Maraging peak-aged at 480°C were approximately equivalent in all the conditions, whereas the curves related to the Maraging peak-aged at 535°C differed slightly both for time to failure and sustained load. Furthermore, it was observed that all Maraging 250 specimens presented ductile necking like the one showed in Fig. 4 (b). Results from scanning electron in microscopy (SEM) analysis are shown in Figures 5 to 10 for the most significant tests. According to fracture surfaces of Fig. 5, test in air for AISI 4340 resulted in a ductile rupture. Conversely, Fig. 6 displays a brittle fracture for AISI 4340 specimens loaded after paint-stripper application. SEM analysis on Maraging 250 surface fractures confirmed what was visible at naked eye in Figure 4 (b), that is all the specimens failed with a cup-cone fracture as visible in Figures from 7 to 9 independently of the test environment. Material Time to failure [s] Air 3.5% NaCl 3.5% NaCl + coupling Paint- stripper AISI 4340 2490 607 675 551 Maraging 250 (peak-aged at 480°C) 1833 1687 1737 1745 Maraging 250 (peak-aged at 535°C) 3563 4175 2940 3100 Table 2 : Average (3 specimens) example of measured time to failure for SSRT conducted on the three materials loaded in different environments. Figure 2 : Stress-Time to Failure curves for AISI 4340. R