Issue 16

L. Susmel, Frattura ed Integrità Strutturale, 16 (2011) 5-17; DOI: 10.3221/IGF-ESIS.16.01 10 Material Reference  A  A  UTS Loding Path [MPa] [MPa] [MPa] 0.1% C steel (normalised) [1] 268.6 151.3 430.7 B-T 0.4% C steel (normalised) [1] 331.9 206.9 648.4 B-T 0.4% C steel (spheroidized) [1] 274.8 155.9 477.0 B-T 0.9% C steel (pearlitic) [1] 352.0 240.8 847.5 B-T 3% Ni steel [1] 342.7 205.3 526.4 B-T 3/3.5% Ni steel [1] 444.7 267.1 722.5 B-T Cr-Va steel [1] 429.1 257.8 751.8 B-T 3.5% NiCr steel (n. impact) [1] 540.3 352.0 895.3 B-T 3.5% NiCr steel (l. impact) [1] 509.4 324.2 896.9 B-T NiCrMo steel (60-70 tons) [1] 602.1 337.7 1000.3 B-T NiCrMo steel (75-80 tons) [1] 660.7 342.7 1242.7 B-T NiCr steel [1] 772.3 452.3 1667.2 B-T SILAL cast iron [1] 240.8 219.2 240.9 B-T NICROSILAL cast iron [1] 253.2 211.5 256.8 B-T S65A Steel [30] 583.5 370.5 1000.8 B-T Cast alloy steel [30] 366.8 247.5 721.2 B-T CuCr cast iron [31] 251.0 198.6 445.4 B-T Inoculated cast iron [31] 177.9 157.2 321.3 B-T NiCr cast iron [31] 146.2 122.7 259.2 B-T CrMo steel (Solid samples) [32] 713.2 425.3 946.5 B-T CrMo steel (Hollow samples) [32] 688.9 412.8 946.5 B-T CrMo steel [32] 509.0 306.9 954.0 B-T CrMo steel [32] 589.6 367.6 944.8 B-T CrMo steel [32] 593.3 350.7 944.8 B-T CrMo steel [32] 628.3 366.6 954.0 B-T NiCrMo steel S81 [32] 589.7 331.9 1103.8 B-T NiCrMoVa steel [32] 660.7 342.7 1242.7 B-T CrMoVa steel DTD551 [32] 667.8 398.3 1397.1 B-T CrMoVa steel DTD551 [32] 659.9 386.5 1397.1 B-T CrMoVa steel DTD551 [32] 706.1 412.5 1368.7 B-T CrMoVa steel DTD551 [32] 737.7 447.4 1368.7 B-T NiCr steel (Solid samples) [32] 666.7 369.7 1389.4 B-T NiCr steel (Hollow samples) [32] 653.2 339.6 1389.4 B-T NiCr steel [32] 771.9 452.3 1667.2 B-T SAE 4340 [33] 462.0 286.0 - B-T Brass [7] 83.4 73.6 319.8 B-T High-strength steel [7] 461.1 274.7 809.3 B-T Nodular Cast Iron [7] 196.2 186.4 476.8 B-T Rolled Steel (Block D) [7] 215.8 137.3 - B-T 0.34% C steel [34] 378.0 218.0 - B-T Carbon Steel [35] 261.0 160.0 - B-T Table 1 : (Caption on the next page).