Issue 13

Ahanchian Mohammad et alii, Frattura ed Integrità Strutturale, 13 (2010) 31-3 5; DOI: 10.3221/IGF-ESIS.13.04 33 C ONVENTIONAL FRACTURE ANALYSIS o numerically predict crack formation and growth of this model under accidental loading, it is necessary to characterize fracture properties at the microscopic level. To approach this objective a complete code of program using finite element method was written by the authors in MathCAD software. The geometrical characteristics, material properties and boundary conditions are attributed to the model. Corresponding finite element analysis was performed to determine the evolution of stress and strain states. For more comprehensible results and better facileness for comparison Von Misses stress had been calculated across the model usin g Eq. (1). (1) According to the theories in Fracture Mechanics, Stress Intensity Factor was calculated throughout the model and was applied to obtain J-integral. According to energy criterion, the critical energy release rate was determined and the crack extension was predicted and is presented in this paper. The breaking force values which lead the crack to propagate were obtained using Trial and Error Method for each case. The model will start propagation at low stresses and tends to extend at the tip of the crack [10, 11]. If the region be plastic at the tip of the crack, the metal mass around the crack would support the stress and the structure is not endangered [12]. Recent work on microstructure silica optical fibers indicated that they failed in a brittle manner and cracks initiated from the fiber surfaces [13]. According to the results, crack will propagate on the brittle area which is glass. The initiation and propagation of crack through brittle materials is at great speeds near the speed of sound [14]. Afterwards, thermal conditions were imposed and the complete procedure was done again. Based on the results, it is studied that crack will not growth anymore when the model is subjected to breaking force and thermal condition. Moreover, the largest crack needs less force to be broken. The contour plots for maximum crack length solved by MathCAD are presented in Fig 2. Fig 2.a shows Von Misses stress distribution subject to critical loading. Based on the data the highest amount of equivalent stress is placed near the crack tip. Fig 2.b p resents Von Misses stress distribution subject to critical loading and thermal conditions. It is shown that the maximum amount of equivalent stress is decreased after applying thermal conditions which prevents crack propagation and material failure. The approximation of crack propagation subject to critical loading is illustrated in Fig 2.c. (a) (b) (c) Figure 2 : Contour plots for maximum crack length (critical length), solved by MathCAD, (a) Von Misses stress distribution subject to critical loading, (b) Von Misses stress distribution subject to critical loading and thermal conditions, (c) Approximation of crack propagation subject to critical loading. The red region i n Fig. 2.a shows the highest amount of equivalent stress. It is placed at the crack tip due to the fact that stresses concentrate at the crack tip. In Fig. 2.b the reduction of maximum amount of equivalent stress is a result of temperature. The prediction of crack propagation is presented by red region i n Fig 2.c. It shows that crack will propagate in silica that is a brittle material meaning that it fractures rather than deforming plastically. It responses to increasing mechanical load until a slow-growing microscopic crack exceeds a certain threshold at which point the crack grows rapidly and the material fractures [3]. T ) (6 ) ( ) ( ) ( 2 1 2 2 2 2 2 2 zx yz xy x z z y y x eq                    