Issue 13

F. Iacoviello et alii, Frattura ed Integrità Strutturale, 13 (2010) 3-16; DOI: 10.3221/IGF-ESIS.13.01 11 Figure 38 : Pearlitic DCI (R = 0.5,  K = 10 MPa√m). Figure 39 : Pearlitic DCI (R = 0.75,  K = 8 MPa√m). Figure 40 : Pearlitic DCI (R = 0.1,  K = 16 MPa√m). Figure 41 : Ferritic-pearlitic DCI (R = 0.1,  K = 15 MPa√m). Figure 42 : Ferritic-pearlitic DCI (R = 0.1,  K = 18 MPa√m). Figure 43 : Ferritic-pearlitic DCI (R = 0.75,  K = 8 MPa√m). Figure 44 : Ferritic-pearlitic DCI (annealed pearlitic DCI) (R = 0.5,  K = 6 MPa√m). Figura 45 : Ferritic-pearlitic DCI (annealed pearlitic DCI) (R = 0.75,  K = 7 MPa√m). Figura 46 : Ferritic-pearlitic DCI (annealed pearlitic DCI) (R = 0.1,  K = 12 MPa√m). Figura 47 : Austempered DCI (R = 0.5,  K = 12 MPa√m). Figura 48 : Austempered DCI (R = 0.1,  K = 6 MPa√m). Figura 49 : Austempered DCI (R = 0.1,  K = 18 MPa√m).