Issue 12

A. Risitano et alii, Frattura ed Integrità Strutturale, 12 (2010) 88-99; DOI: 10.3221/IGF-ESIS.12.09 95 Figura 10 : Incremento di temperatura T in funzione del numero di cicli per acciaio C40 (f=10 Hz, R=-1) per differenti serie (I, II, III). Figura 11 : Andamenti del  T di temperature in funzione del numero di cicli (f=10 Hz, R= -1) per differenti serie (I, II, III). C40-14KN(10Hz) -1,0 -0,5 0,0 0,5 1,0 1,5 2,0 2,5 3,0 3,5 0 2 4 6 8 10 12 Cyclesx1000  T l Serie ll Serie lll Serie C40-17KN(10Hz) -1,0 0,0 1,0 2,0 3,0 4,0 5,0 6,0 0 2 4 6 8 10 12 Cyclesx1000  T l Serie ll Serie lll Serie C40 - 20KN(10Hz) 0,0 2,0 4,0 6,0 8,0 10,0 12,0 14,0 16,0 0 2 4 6 8 10 12 Cyclesx1000  T l Serie ll Serie lll Serie C40 - 23 KN (10 Hz) 0,0 5,0 10,0 15,0 20,0 25,0 30,0 0 2 4 6 8 10 12 Cycles x 1000  T l Serie ll Serie lll Serie C40 - 26KN (10Hz) 0,0 10,0 20,0 30,0 40,0 50,0 60,0 70,0 80,0 90,0 0 5 10 15 Cyclesx1000  T l Serie ll Serie lll Serie ri Seri Serie rie S ri S