The present paper deals with the determination of the critical value of the J-integral by the method
of the deep crack on specimens in aluminum 6060 in bending. Following a first step in which the traditional
methodologies were used, the Digital Image Correlation (D.I.C.) technique was used in order to determine the
Crack Tip Opening Displacement with different values of the crack propagation. The experimental analysis was
performed following the three phases of the deep crack methodology: pre-cracking in dynamic conditions, crack
propagation under static loading, dynamic failure. The images acquired by the D.I.C. techniques showed values
of the CTOD similar to those found with the traditional techniques.
SOMMARIO. Nel presente lavoro è stato determinato il valore critico dell’integrale J mediante il metodo della
cricca profonda su provini di alluminio 6060 in flessione. Dopo una prima analisi sulla base delle metodologie
tradizionali, è stata usata la Digital Image Correlation (D.I.C.) per determinare il CTOD per differenti valori
della propagazione della frattura L’analisi sperimentale è stata eseguita pre-criccando il provino in condizioni
dinamiche, quindi procurando la propagazione della cricca in condizioni statiche, infine producendo la rottura
sotto carico dinamico. Le immagini acquisite mediante D.I.C. mostrano valori del CTOD simili a quelle rilevate
con le tecniche tradizionali.